Customization: | Available |
---|---|
After-sales Service: | Installation Guide |
Warranty: | 2 Years After Leaving The Factory |
Still deciding? Get samples of $ !
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment Methods: |
![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() |
---|---|
Support payments in USD |
Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
High damping rubber bearing, also called HDR bearing pad, is one of seismic isolation bearing. It has excellent seismic isolation performance to effectively reduce the bridge damage caused by earthquake.
HDR bearing pad is composed of specialized designed rubber with high damping performance, sandwiched together with steel plate layer. When installing, the high damping rubber bearing is commonly used with top and bottom steel plate and connection accessories.
During earthquake, the vibration from various directions will impact fixed base building and results in deformation and building or bridge damages. The high damping bearing pad is improved through high damping material, which the damping ratio can approach to 15% to 18%.
When the earthquake comes, the high damping rubber bearing will increase the horizontal displacement through rubber shear deformation and reduce friction coefficient. The large displacement can weaken the vibration from all direction and reduce the damage of building and bridges.
Joint structure
Specifications
Damping ratio:
Characteristics | Requirements | |||
---|---|---|---|---|
G Modulus (MPa) | 0.7 | 0.9a | 1.15 | |
Tensile strength (MPa) | Moulded Test Piece | ≥16 | ≥16 | ≥16 |
Test Piece From Bearing | ≥14 | ≥14 | ≥14 | |
Minimum Elongation at Break (%) | Moulded Test Piece | 450 | 425 | 300 |
Test Piece from Bearing | 400 | 375 | 250 | |
Minimum Tear Resistance (kN/m) | CR | ≥7 | ≥10 | ≥12 |
NR | ≥5 | ≥8 | ≥10 | |
Compression Set (%) | CR 24 h, 70 °C | ≤15 | ||
NR 24 h, 70 °C | ≤30 | |||
Accelerated Ageing (Maximum change from unaged value) | ||||
Hardness (IRHD) | NR 7d, 70 °C | -5+10 | ||
CR 3d, 100 °C | ±5 | |||
Tensile strength (%) | NR 7d, 70 °C | ±15 | ||
CR 3d, 100 °C | ±15 | |||
Elongation at break (%) | NR 7d, 70 °C | ±25 | ||
CR 3d, 100 °C | ±25 | |||
Ozone Resistance | Elongation: 30%, 96 h | No cracks | ||
40±2 °C | ||||
NR 25 pphm | ||||
CR 100 pphm |
Feature: