| Customization: | Available |
|---|---|
| After-sales Service: | Installation Guide |
| Application: | Construction Concrete Joint, Expanding Joint |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Physical properties | Test methods | SBR | High tensile neoprene rubber | Natural rubber |
Water absorption 2 days at 70°C (% change) | ASTM D-471 | 5% (max) | 5% (max) | 5% (max) |
Hardness shore A | ASTM D-2240 | 65 | 65 | 65 |
Tensile strength | ASTM D- 412 | 3000 psi (min) | 2500 psi (min) | 3500 psi (min) |
Tensile strength at 300% Modulus | ASTM D-412 | 1150 psi (min) | 1150 psi (min) | 1450 psi (min) |
Ultimate elongation | ASTM D-412 | 450% (min) | 450% (min) | 500% (min) |
Compression set 22 hours at 70°C (% original deflection) | ASTM D-395 | 30% (max) | 40% (max) | 30% (max) |
Accelerated aging 96 hours at 70°C (% of tensile strength before aging) | ASTM D-573 | 80% (min) | 80% (min) | 80% (min) |
Accelerated aging 96 hours at 70°C (% of elongation before aging) | ASTM D-573 | 80% (min) | 80% (min) | 80% (min) |
Ozone resistance 7 days at 50 PPHM at 70°C, 20% elongation | ASTM D-1149 | No crack | No crack | No crack |